Preparation of chitosan-PE antimicrobial bi-layer films and antibacterial activity
-
摘要: 结合壳聚糖良好的成膜性和广谱抑菌性及PE膜较好的机械强度和阻隔性,制备壳聚糖-PE双层抑菌保鲜膜。通过单因素实验和Box-Behnken Design实验设计考察壳聚糖、醋酸、甘油和Span 40浓度对膜的抗拉强度和断裂伸长率的影响;得到膜液最佳组合为:壳聚糖浓度0.94%、醋酸浓度0.49%、甘油浓度1.07%、Span 40浓度1.41%,所得膜的抗拉强度和断裂伸长率分别为3.59MPa和116.72%;最后研究了壳聚糖-PE双层抑菌保鲜膜对大肠杆菌(E.Coli)和金黄色葡萄球菌(B.Subtilis)的抑菌性,结果表明,此保鲜膜对大肠杆菌和金黄色葡萄球菌的抑菌率分别可达80.77%和93.02%。Abstract: Chitosan-PE films were prepared by combining the excellent film property and antimicrobial activity of chitosan with good mechanical and barrier properties of PE film. The effect of the concentration of chitosan, acetic acid, glycerol (Gly) and Span 40 on tensile strength (TS) and elongation at break (E) were investigated.The optimum combine ingredients were obtained through single factor experiments and Box-Behnken Design, which were 0.94% chitosan, 0.49% acetic acid, 1.07% Gly and 1.41% Span 40. TS and E of chitosan-PE bi-layer films were 3.59MPa and 116.72%, respectively. Also, the antibacterial activity against E. Coli and B. Subtilis of the film were measured. Results showed that the antibacterial ratio was 80.77% and 93.02%, respectivedly.
-
Keywords:
- chitosan /
- PE film /
- response surface methodology /
- antibacterial activity
-
[1] 岳晓华, 沈月新.可食性壳聚糖膜性能的研究[J].食品科学, 2002, 23 (8) :62-67. [2] Tripathi S, Mehrotra G K, Dutta P K.Physicochemical and bioactivity of cross-linked chitosan-PVA film for food packaging applications[J].International Journal of Biological Macromolecules, 2009, 45 (4) :372-376.
[3] Aider M.Chitosan application for active bio-based films production and potential in the food industry:Review[J].LWTFood Science and Technology, 2010, 43 (6) :837-842.
[4] Prashanth H KV, Tharanathan R N.Chitin/Chitosan:modification and their unlimited application potential-an overview[J].Trend in Food Science and Technology, 2007, 18 (3) :117-131.
[5] 郑连英, 朱江峰, 孙昆山.壳聚糖的抗菌性能研究[J].材料科学与工程, 2000, 18 (2) :22-24. [6] 吴丽颖, 刘建芳, 候艳宁.壳聚糖在药物制剂中的应用[J].解放军医药杂志, 2012, 24 (4) :48-52. [7] 黄燕, 刘力.壳聚糖保鲜研究及其在冷却肉保鲜中的应用[J].动物医学进展, 2010, 31 (S1) :63-65. [8] 贾秀春, 吴凤娜, 李迎秋, 等.壳聚糖在冷却肉保鲜中的应用[J].山东轻工业学院学报, 2012, 26 (1) :9-12. [9] Wang S, Shen L, Tong Y, et al.Biopolymer chitosan/montmorillonite nanocomposites:preparation and characterization[J].Polymer Degradation and Stability, 2005, 90 (1) :123-131.
[10] Xu Y, Ren X, Hanna M.Chitosan/clay nanocomposite film preparation and characterization[J].Journal of Applied Polymer Science, 2006, 99 (4) :1684-1691.
[11] 程强, 刘思莹, 曲美, 等.PO膜和PE膜日光温室温光环境比较[J].中国蔬菜, 2011, 24 (22) :72-77. [12] Robertson G L.Editor.Food packaging principles and practice[M].Boca Raton:CRC Press, 2006:16-18.
[13] 杨远宜.抗菌保鲜膜研究及进展[J].包装工程, 2007, 28 (6) :201-203. [14] 宋慧君, 孟春丽, 汤克勇.明胶-壳聚糖复合膜的制备与性能[J].高分子材料科学与工程, 2011, 27 (8) :165-167. [15] 赵素芬, 潘斌, 刘晓艳.壳聚糖复合保鲜膜制备及其拉伸性能研究[J].包装工程, 2012, 33 (1) :5-7. [16] 徐晶, 侯菲.可食性食品保鲜膜的研制[J].食品科学, 2011, 32 (10) :312-315. [17] 李爱珍.明胶-壳聚糖可食性复合膜的制备及应用研究[D].济南:山东轻工业学院, 2010. [18] 孟晓荣, 张敏, 胡新婷.壳聚糖对食品中常见菌的抑制作用[J].食品与机械, 2007, 23 (2) :90-92. [19] 李家政, 毕大鹏, 李杨.聚乙烯果蔬保鲜膜的透气和透湿性能与温度变化的关系[J].保鲜与加工, 2009 (5) :30-33. [20] 谭绍早, 张红, 陈震华.PE抗菌食品保鲜膜的研制[J].塑料工程, 2003, 31 (10) :51-53. [21] Dutta P K, Tripathi S G K, MehrotraG K, et al.Perspectives for chitosan based antimicrobial films in food applications[J].Food Chemistry, 2009, 114 (4) :1173-1182.
[22] 杨东芝, 刘晓菲, 李治, 等.壳聚糖抗菌活性的影响因素[J].应用化学, 2000, 17 (6) :598-602.
计量
- 文章访问数:
- HTML全文浏览量:
- PDF下载量: